EPOXY BASED THIXOTROPIC (ORANGE PEEL TEXTURE)

QIS FLOOR EP SL, two component, epoxy based and specially formulated for industrial areas, smooth surface finish, easy to clean,thixotropic,textured look like orange peel. 

 High mechanical strength

 Glossy surface
 Easy to apply.

 It is easy to clean and maintain.
 Non-slip surface can be obtained.

Where to use?

 On concrete and cement based surfaces,
 warehouses, storages
 industrial facilities,
 shopping centers,
 exhibition and fair areas
 car parks.
 

How to use?

Before the application, the surface should be cleaned from substances that prevent adhesion such as dust, oil, paint, curing.

The moisture on the surface should not be over 5%. 
Concrete must have been applied at least 28 days ago. 
Before the application, the surface must not be watered and the surface must be dry.
Cracks in concrete and parts that need repair should be repaired with suitable products.
Before application, the surface should be primed with suitable epoxy based primers. Before the primer layer, the surface should be roughened by suitable mechanical methods.
Mixing
A component and B component are in separate packages with clarified mixing ratios. Component B is completely poured into component A and mixed. 
Mixing should be done with a mixer at 300 rpm.
It is a two-component product and should be prepared in the specified mixture ratio, considering the pot life, as much as the amount to be consumed.

In order to obtain a homogeneous mixture, the product temperature should not be less than 15°C.
Component A should be mixed with a mechanical mixer, and hardener (component B) should be added by considering to the mixing ratio.
A and B components should be mixed with a mechanical mixer for at least 3 minutes until homogeneous. 
The mixture should be consumed within 20 minutes.

The mixture is poured onto the surface and spread with a trowel.Roll up and down both directions for finishing texture.
The material that spreads completely on the surface is accelerated by the roller.
It is recommended to wear spiked shoes so that the surface does not deteriorate during the application.