EPOXY BASED SELF-FLOORING

QIS FLOOR EP SL, two component, epoxy based and specially formulated for industrial areas, smooth surface finish, easy to clean, self-leveling.

 High mechanical strength

 Due to its self-leveling feature, it can be applied on sandy or sand-free smoothly

 Easy to apply.
 Production available in optional color.

Where to use?

 On concrete and cement based surfaces,
 warehouses, storages
 industrial facilities,
 shopping centers,
 exhibition and fair areas
 car parks.
 

How to use?

Before the application, the surface should be cleaned from substances that prevent adhesion such as dust, oil, paint, curing.
The moisture on the surface should not be over 5%. 
Concrete must have been applied at least 28 days ago. 
Before the application, the surface must not be watered and the surface must be dry.
Cracks in concrete and parts that need repair should be repaired with suitable products.
Before application, the surface should be primed with suitable epoxy based primers. Before the primer layer, the surface should be roughened by suitable mechanical methods.
Mixing
A component and B component are in separate packages with clarified mixing ratios. Component B is completely poured into 
component A and mixed. 
Mixing should be done with a mixer at 300 rpm.
It is a two-component product and should be prepared in the specified mixture ratio, considering the pot life, as much as the amount to be consumed.

In order to obtain a homogeneous mixture, the product temperature should not be less than 15°C.
Component A should be mixed with a mechanical mixer, and hardener (component B) should be added by considering to the mixing ratio.
A and B components should be mixed with a mechanical mixer for at least 3 minutes until homogeneous. 
The mixture should be consumed within 20 minutes.

Ready to use mixture is applied in both directions.Epoxy-based primers should be used before its application,if the product is to be used as a coating material directly on the floor.There is no need for re-primer application when it will be applied as a top coat paint on the epoxy coating system.The application is done in two coats and the second coat should be applied within 24 hours.